BaTiO3 (001) 5x5x1.0 mm, 1SP, Substrate grade with single domain

Crystal Structure

• Tetragonal ( 4m) : 9^oC < T < 130.5 ^oC
• a=3.99  A  c= 4.04 A

Growth Method

Top Seeded Solution Growth

Melting Point

1600 ^oC

Density

 6.02  g/cm³

Dielectric constants

• e_a = 3700, e_c = 135 (unclamped)
• e_a = 2400, e _c = 60 (clamped)

Index of Refraction

•                 515 nm               633 nm     800 nm
• n_o            2.4921                   2.4160                   2.3681
• n_e            2.4247                   2.3630                   2.3235

Transmission wavelength

0.45 ~ 6.30 mm

Electro Optic Coefficients:

r^T ₁₃ =      11.7 ?1.9 pm/V     r^T ₃₃ =112 ?10  pm/V    r^T ₄₂=       1920 ?180  pm/V

Reflectivity of SPPC
( at 0 deg. cut )

• 50 - 70 % ( max. 77% ) for l = 515 nm
• 50 - 80 % ( max: 86.8%) for l = 633 nm

Absorption loss: 

• l:             515 nm               633 nm                   800 nm
• a:            3.392cm^-1              0.268cm^-1              0.005cm^-1