Precursor Powder of (Ni0.8Co0.15Al0.05(OH)2 for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA

RM0.00 MYR

Precursor Powder of (Ni0.8Co0.15Al0.05(OH)2 for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA

Name: Precursor Powder of (Ni0.8Co0.15Al0.05(OH)2 for DIY High Capacity Li-Ion Battery Cathode Powder 200g/bottle - EQ-Lib-Pre-NCA
Brand: MTI
SKU: Lib-PNCA
Availability: OutOfStock

SKU: precursor-powder-of-ni0-8co0-15al0-05oh2-for-diy-high-capacity-li-ion-battery-cathode-powder-200g-bottle-eq-lib-pre-nca

Price: RFQ

Description

EQ-Lib-Pre-NCA is the precursor of NCA (Ni0.8Co0.15Al0.05 (OH)2) for DIY Li--NCA cathode powder for high capacity Li-Ion cathode at your own composition. Note: You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use Specification Package 200g/bottle in a vacuumed bag Composition Ni 0.8 Co 0.15 Al 0.05 OH 2 Configuration Sphere Particle size distribution D105±0.5μm D5013-18μm D9030±0.5μm Specific surface area ~1.5m2/g Tap Density ≥1.8g/cm3 Water Content 500ppm PPH value ≤11.2 Mian Element Required Content Real Content% Li 0 0 Ni 80±0.5 80.07 Co 15±0.5 15.10 Al 5±0.5 4.77 Impurity Requiredppm Typicalppm Ca 300 49.58 Cu 50 ND Fe 100 96.34 Cr 50 27.51 Mg 300 44.56 Na 500 119.85 S 2000 391.5 Zn 100 4.19 Mn 100 29.98 Si 300 75.23 Zr 5000 390.0 Y 250 170.12 Note MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have the question for IP, we will forward your inquiry to the producer. Application Notes : Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry. Please keep the powder in a vacuum box to avoid moisture. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity. Related Products Vacuum Storage Box Powder Milling & Mixer Electrode Coaters Battery Research Equipment Other Battery Powders Solid Electrolyte

Package	200g/bottle in a vacuumed bag
Composition	Ni_0.8Co_0.15Al_0.05OH₂
Configuration	Sphere
Particle size distribution	D105±0.5μm D5013-18μm D9030±0.5μm
Specific surface area	~1.5m2/g
Tap Density	≥1.8g/cm3
Water Content	500ppm
PPH value	≤11.2
Mian Element	Required Content	Real Content%
Li	0	0
Ni	80±0.5	80.07
Co	15±0.5	15.10
Al	5±0.5	4.77
Impurity	Requiredppm	Typicalppm
Ca	300	49.58
Cu	50	ND
Fe	100	96.34
Cr	50	27.51
Mg	300	44.56
Na	500	119.85
S	2000	391.5
Zn	100	4.19
Mn	100	29.98
Si	300	75.23
Zr	5000	390.0
Y	250	170.12
Note	MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have the question for IP, we will forward your inquiry to the producer.