Lithium Phosphorus Sulfur Chloride (Li6PS5Cl or Sb-Li6PS5Cl) Powder as Solid-State Electrolyte for Li-ion Battery, 10g/bottle-Lib-LPSCI

Pristine, 10g/bottle

RM0.00 MYR

Lithium Phosphorus Sulfur Chloride (Li6PS5Cl or Sb-Li6PS5Cl) Powder as Solid-State Electrolyte for Li-ion Battery, 10g/bottle-Lib-LPSCI

SKU: lib-lpsci

Price: RFQ

Description

Antimony-doped Lithium Phosphorus Sulfur Chloride (Sb-Li6PS5Cl) Powder as solid-state electrolyte for Li-ion Battery Research & Education, 10g or 20g/bottle - Lib-LPSCI Specification Product Name Lithium Phosphorus Sulfur Chloride or Antimony-doped one Chemical Formula Li6PS5Cl, or Sb-Li6PS5Cl Theoretical Density 1.64g/cm^3 Appearance Orange Powder Powder Distribution 2 ~ 10 um Ionic Conductivity 2mS/cm (25°C, 300MPa) Electronic Conductivity ≤1 x 10^-8 S/cm Working Humidity Environment Dew point -40°C or above SEM Li6PS5Cl Sb-Li6PS5Cl XRD Impedance Spectrum Arrhenius Curve Application Notes : Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry. Please keep the powder in the vacuum box to avoid moisture. Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity. The product is for research only, not supply for large quantity, Related Products Vacuum Storage Box Powder Milling & Mixer Electrode Coaters Battery Research Equipment Other Battery Powder Solid Electrolyte

Product Name	Lithium Phosphorus Sulfur Chloride or Antimony-doped one
Chemical Formula	Li6PS5Cl, or Sb-Li6PS5Cl
Theoretical Density	1.64g/cm^3
Appearance	Orange Powder
Powder Distribution	2 ~ 10 um
Ionic Conductivity	2mS/cm (25°C, 300MPa)
Electronic Conductivity	≤1 x 10^-8 S/cm
Working Humidity Environment	Dew point -40°C or above
SEM	Li6PS5Cl Sb-Li6PS5Cl
XRD
Impedance Spectrum
Arrhenius Curve